Photodegradation and photostabilization of polymers, especially polystyrene: review.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

REVIEW

a SpringerOpen Journal

Open Access

Photodegradation and photostabilization of polymers, especially polystyrene: review Emad Yousif* and Raghad Haddad

Abstract Exposure to ultraviolet (UV) radiation may cause the significant degradation of many materials. UV radiation causes photooxidative degradation which results in breaking of the polymer chains, produces free radical and reduces the molecular weight, causing deterioration of mechanical properties and leading to useless materials, after an unpredictable time. Polystyrene (PS), one of the most important material in the modern plastic industry, has been used all over the world, due to its excellent physical properties and low-cost. When polystyrene is subjected to UV irradiation in the presence of air, it undergoes a rapid yellowing and a gradual embrittlement. The mechanism of PS photolysis in the solid state (film) depends on the mobility of free radicals in the polymer matrix and their bimolecular recombination. Free hydrogen radicals diffuse very easily through the polymer matrix and combine in pairs or abstract hydrogen atoms from polymer molecule. Phenyl radical has limited mobility. They may abstract hydrogen from the near surrounding or combine with a polymer radical or with hydrogen radicals. Almost all synthetic polymers require stabilization against adverse environmental effects. It is necessary to find a means to reduce or prevent damage induced by environmental components such as heat, light or oxygen. The photostabilization of polymers may be achieved in many ways. The following stabilizing systems have been developed, which depend on the action of stabilizer: (1) light screeners, (2) UV absorbers, (3) excited-state quenchers, (4) peroxide decomposers, and (5) free radical scavengers; of these, it is generally believed that excited-state quenchers, peroxide decomposers, and free radical scavengers are the most effective. Research into degradation and ageing of polymers is extremely intensive and new materials are being synthesized with a pre-programmed lifetime. New stabilizers are becoming commercially available although their modes of action are sometimes not thoroughly elucidated. They target the many possible ways of polymer degradation: thermolysis, thermooxidation, photolysis, photooxidation, radiolysis etc. With the goal to increase lifetime of a particular polymeric material, two aspects of degradation are of particular importance: Storage conditions, and Addition of appropriate stabilizers. A profound knowledge of degradation mechanisms is needed to achieve the goal.

Introduction Exposure to ultraviolet (UV) radiation may cause significant degradation of many materials. UV radiation causes photooxidative degradation which results in breaking of the polymer chains, produces radicals and reduces the molecular weight, causing deterioration of mechanical properties and leading to useless materials, after an unpredictable time. Polystyrene (PS), one of the most important materials from the modern plastic industry, has been used all over * Correspondence: [emailprotected] Department of Chemistry, College of Science, Al-Nahrain University, Baghdad, Iraq

the world, due to its excellent physical properties and low-cost. Rabie et al. (2008). When polystyrene is subjected to UV irradiation in the presence of air, it undergoes a rapid yellowing and a gradual embrittlement Geuskens and David (1975). The mechanism of PS photolysis in the solid state (film) depends on the mobility of radicals in the polymer matrix and their bimolecular recombination. Hydrogen radicals diffuse very easily through the polymer matrix and combine in pairs or abstract hydrogen atoms from polymer molecule. The phenyl radical has limited mobility. It may abstract hydrogen from the near surrounding or combine with a polymer radical or with hydrogen radicals.

© 2013 Yousif and Haddad; licensee Springer. This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Almost all synthetic polymers require stabilization against adverse environmental effects. It is necessary to find a means to reduce or prevent damage induced by environmental components such as heat, light or oxygen Rabek and Ranby (1974a, 1974b). The photostabilization of polymers may be achieved in many ways. The following stabilizing systems have been developed, which depend on the action of stabilizer: (1) light screeners, (2) UV absorbers, (3) excited-state quenchers, (4) peroxide decomposers, and (5) radical scavengers; of these, it is generally believed that excited-state quenchers, peroxide decomposers, and radical scavengers are the most effective Yousif et al. (2013). Research into degradation and ageing of polymers is extremely intensive and new materials are being synthesized with a pre-programmed lifetime. New stabilizers are becoming commercially available although their modes of action are sometimes not been thoroughly elucidated. They target the many possible ways of polymer degradation: thermolysis, thermooxidation, photolysis, photooxidation, radiolysis, etc. With the goal for increasing lifetime of a particular polymeric material, two aspects of degradation are of particular importance: storage conditions, and addition of appropriate stabilizers. A profound knowledge of degradation mechanisms is needed to achieve the goal. Definitions & historical aspects of photodegradation of polymers

Polymers are a broad class of materials which are made from repeating units of smaller molecule called monomers. Polymers can be natural in origin such as the lignin of tree branches. Other polymers are termed synthetic, because they are made by humans from naturally-occurring materials. Example such as polyester and polystyrene. Polymers are useful because of their strength and durability in many applications. One of the disadvantages of using polymers is that they degrade when they are used in high temperature conditions or in outdoor applications. When polymers are used in outdoor applications, the environment negatively influences the servicelife. This process is called weathering (Zweifel 1998; Wypych 2008). The term degradation of macromolecules denotes all processes which lead to a decline of polymer properties. It may eventually involve physical processes, such as polymer recrystallization, or denaturation of protein structures. Chemical processes related to degradation may lead to a reduction of average molar mass due to macromolecular chain bond scission or to an increase of molar mass due to crosslinking rendering the polymer insoluble. The term ageing of polymers is usually associated with long-term changes of polymer properties under

Page 2 of 32

the conditions of weathering and may involve any of the above processes Strlic & Kolar (2005). A wide variety of synthetic and naturally occurring high polymers absorb solar ultraviolet radiation and undergo photolytic, photooxidative, and thermooxidative reactions that result in the degradation of the material (Ayako and Hirose 1999; Scott 2000; Valkoa et al. 2001). In recent years, the use of polymeric materials has rapidly increased but it is well established that rapid photodegradation of these materials is possible when they are exposed to natural weathering (Guillet 1985; Hamid 2000; Rabek 1996; Bottino et al. 2003). This is a serious issue, with economic and environmental implications and therefore a large effort is focused on understanding the changes that occur at molecular level and the degradation kinetics. Following different routes, UV radiation causes a photooxidative degradation which results in breaking of the polymer chains, produces radical and reduces the molecular weight, causing deterioration of mechanical properties and leading to useless materials, after an unpredictable time (Bottino et al. 2003; Gardella 1988). Exposure to ultraviolet, UV, radiation may cause the significant degradation of many materials. Damage by UV radiation is commonly the main reason for the discoloration of dyes and pigments, weathering, yellowing of plastics, loss of gloss and mechanical properties (cracking), sun burnt skin, skin cancer, and other problems associated with UV light. The manufacturers of paints, plastics, contact lenses, and cosmetics have a great interest in offering products that remain unaltered for long periods under conditions of light exposure (Galdi et al. 2010; Pospisil et al. 2006; Bojinov & Grabchev 2005; Goldshtein and Margel 2011), (Figure 1). Most of the common polymers used in such applications contain photostabilizers to reduce photodamage and to ensure acceptable life times under outdoor exposure conditions. The use of plastics in building applications is popular in the developing world because of the low cost and the ease of use of plastic components compared to the conventional metal, glass, mortar, wood and other materials. Plastics are used in other products such as outdoor furniture, fishing gear, and marine craft, which are also routinely used outdoors (Andrady 1997; Sampers 2002). Solar radiation reaching the surface of the earth is characterized by wave lengths from approximately 295 up to 2500 nm. The solar radiation classified as UV-B (280 – 315 nm) has an energy of 426 – 380 KJ mol-1. Fortunately, the higher energetic part of UV-B; 280 – 295 nm, is filtered by the stratosphere and does not reach the earth’s surface, UV-A (315 – 400 nm), has energy between 389 and 300 KJ mol-1 and is less harmful for organic materials than UV-B. Visible (400 – 760 nm).

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 3 of 32

(i)Chain initiation: Hydroperoxide (POOH) Carbonyl compounds (c=o)

heat , hv P.,POO.,OH.,HO . radical 2 M+2 , M+3

Catalyst residue (Tin , V+n etc) Charge transfer complexes (PH , O2)

(ii)Chain propagation: heat , hv . P + O2 M +2 , M+3 . heat , hv POO + PH

POO

POOH + P

M+2 , M+3

. . PO + OH . POO + PO +

POOH 2POOH .

PO + PH . HO + PH

POH + P H2 O + P

. .

(iii)Chain termination: . . P +P . . P + POO . . POO + POO

non radical products

e.t.c Where P. is polymer radical , M+ is metal ion , and PH is polymer molecule

Figure 1 General oxidation & photooxidation in polymers, (Rabek 1994).

and infrared (760 – 2500nm.) Pospisil and Nespurek (2000). Photooxidation of organic materials is a major cause of irreversible deterioration for a large number of substances. It is responsible not only for the loss of physical properties of plastics, rubber, but also for foodstuffs Grassie and Scott (1985). In most polymers photooxidative degradation may be induced by UV radiation or catalytic process (or both) and can be accelerated at elevated temperature. Factors causing the photodegradation

Generally, many factors are responsible for causing photodegradation of polymeric materials. They may be divided into two categories: Schnabel (1981) I) Internal impurities, which may contain chromophoric groups that are introduced into macromolecules during polymerization processing and storage; they include: a- Hydroperoxide. b- Carbonyl.

c- Unsaturated bonds (C=C). d- Catalyst residue. e- Charge–transfer (CT) complexes with oxygen. II) External impurities, which may contain chromophoric groups, are: a- Traces of solvents, catalyst, …. etc. b- Compounds from a polluted urban atmosphere and smog, e.g. polynuclear hydrocarbons such as naphthalene and anthracene in polypropylene and polybutadiene. c- Additives (pigments, dyes, thermal stabilizers, photostabilizers, …. etc.). d- Traces of metals and metal oxides from processing equipment and containers, such as Fe, Ni or Cr.

Types of polymers degradation

The degradation of polymers usually starts at the outer surface and penetrates gradually into the bulk of the material Blaga (1980).

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 4 of 32

Polymer degradation can be caused by heat (thermal degradation), light (photodegradation), ionizing radiation (radio degradation), mechanical action, or by fungi, bacteria, yeasts, algae, and their enzymes (biodegradation). The deleterious effects of weathering on polymers generally has been ascribed to a complex set of processes in which the combined action of UV. light and oxygen predominant. The overall light-initiated process in the presence of oxygen generally is referred to as oxidative photodegradation or photooxidation. A pure thermal effect in possible because oxygen is always present and so the process is thermaloxidative degradation Feldman (2002). There are many different modes of polymer degradation. These are very similar since they all involve chemical reactions that result in bond scission. These modes are: Schnabel (1981). Chemical degradation

Chemical degradation refers exclusively to processes, which are induced under the influence of chemical reagent (e.g. acids, bases, solvents reactive gases, etc.) Weidner et al. (1996). Thermal degradation

Thermal degradation refers to the case where the polymer, at elevated temperatures, starts to undergo chemical changes without the simultaneous involvement of another compound Guaita et al. (1985). Biodegradation

Biologically initiated degradation also is strongly related to chemical degradation as far as microbial attack is concerned. Microorganisms produce variety of enzymes which are capable of reaction with natural and synthetic polymers Dindar and Icli, (2001). Radiolytic degradation

When polymeric materials are subjected to high energy radiation (e.g. gamma radiation) changes are observed on their molecular structure, mainly chain scission, which leads to reduction in molar mass Vinhas et al. (2003). Mechanical degradation

This generally, refers to macroscopic effects brought about under the influence of shear forces. These forces result in the formation of macro radicals as follows:

Polymer chain

. . C + C

(1)

Macro free radical

Such radicals can recombine in the absence of oxygen. In the presence of oxygen peroxy radicals may be

formed, which leads to the degradation of polymeric chains Potts (1991).

+ O2

. O

(2)

Photodegradation

Photodegradation is degradation of a photodegradable molecule caused by the absorption of photons, particularly those wavelengths found in sunlight, such as infrared radiation, visible light, and ultraviolet light. However, other forms of electromagnetic radiation can cause photodegradation. Photodegradation includes photodissociation, the breakup of molecules into smaller pieces by photons. It also includes the change of a molecule's shape to make it irreversibly altered, such as the denaturing of proteins, and the addition of other atoms or molecules. A common photodegradation reaction is oxidation. Photodegradation in the environment is part of the process by which ambergris evolves from its fatty precursor. Photodegradation also destroys paintings and other artifacts. Light - induced polymer degradation, or photodegradation, includes the physical and chemical changes caused by irradiation of polymers with ultraviolet or visible light. In order to be effective, light must be absorbed by the substrate (polymeric system). Thus, the existence of chromophoric groups in the macromolecules is a prerequisite for the initiation of any photochemical reaction Schnabel (1981). Ketones, quinines, and peroxides are initiators for different reaction degradation or chemical modification occurring in organic compounds Kaczmarek et al. (1999). They absorb light up to about 380 nm, which causes their excitation or cleavage to radicals. One may initiate polymer degradation and other transformation by abstruction of hydrogen atom from a macromolecule (PH) and formation of polymer alkyl radical (P.) (Rabek 1993; Rabek 1996). The influence of low-molecular weight organic compounds such as benzophenone (BPh), anthraquinone (AQ) and benzoyl peroxide (BPo) on the photoprocesses of polystyrene has been studied. The results indicate that additives accelerate and increase the photodegradation and photooxidation of polystyrene Kaczmarek et al. (1999). Photodegradation may occur in the absence of oxygen (chain breaking or cross-linking) and the presence of oxygen (photooxidative) degradation. The photooxidative degradation process is induced by UV radiation and other catalysts (or both) and can be accelerated at elevated temperatures. Photodegradation of polystyrene (e.g. embrittlement and color change) can take place upon irradiation with a portion of UV light that is contained within sun light.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 5 of 32

Many reviews have been published on photodegradation and photooxidation degradation of polystyrene (Pinto et al. 2013; Gijsman and Diepens 2009; Rabek 1995). The term of photodegradation might be distinguished from photooxidation of the polymer. In the latter, oxygen is involved in the process while in the former light energy (E=hƲ) only is responsible for the photodegradation.

hom*ogeneous liquid phase oxidations Kochi and Wiley (1973), Geuskens & David (1979a, 1979b).

Mechanism of photooxidative degradation of polymers

Photooxidative degradation of polymers, which include processes such as chain scission, crosslinking and secondary oxidative reactions, and takes place via radical processes, similar to thermal oxidation reactions (Ranby and Rabek 1981; Carlsson et al. 1976; Mc Kellar & Allen 1979; Rnby and Lucki 1980). Two mechanisms have been proposed to explain the photooxidation of polymers in conformity with similar observations made on low molecular weight compounds. One proceeds through direct reaction of singlet oxygen with the substrate while the other involves the production of radicals and subsequent reaction with oxygen (Geuskens & David 1979a, 1979b; Trozzolo and Winslow 1968). (I)The singlet oxygen mechanism of oxidation

It has been clearly demonstrated that many photosensitized oxidation reactions proceed with participation of oxygen in an electronically excited singlet state. The photochemical production of singlet oxygen is mainly due to quenching of the excited triplet state of suitable sensitizers: (3) Singlet oxygen exhibits several specific reactions and the one that has been most often invoked in the photooxidation of polymers is the formation of a hydroperoxide by oxidation of an olefin containing an allylic hydrogen, and which could further decompose and lead to chain scission and formation of a terminal of carbonyl group.

C H

1O 2

OOH

(4) (II)The free radical mechanism of oxidation

The radical mechanism of photooxidation of polymers proceeds through a chain reaction similar to that for

Steps of photodegradation

Photooxidative degradation includes the following steps: (Rabek 1994; Rabek 1974; Guillet 1972a, 1972b). Initiation, propagation and termination. These steps are illustrated in the Figure 2: Photoinitiation step

Internal and/or external chromophoric groups absorb light and produce low molecular weight radicals (R.) and /or polymeric macro radicals (P.) as follows: (5) This reaction may be initiated by physical factors such as: UV radiation, heat, ionization, ultrasonic or mechanical effects or by chemical factors (direct reaction with O2 or atomic oxygen, catalysis or singlet O2 [O*2]1 excited state. The “hydroperoxide” (POOH) is the most important initiator in the photooxidative process Grassie and Scott (1985). Whatever the initial mechanism of radical formation, hydroperoxides are produced after reaction with oxygen. These are thus key intermediates in the oxidation of polymers Amin et al. (1975). Moreover, hydroperoxides are extremely photolabile; they usually decompose with quantum yields close to unity to produce radicals that can abstract hydrogen atoms from the polymer and thus initiate the photooxidation: (6) The formation of hydroperoxide and its photolysis illustrate the formation of other effective functional groups such as carbonyl during β-scission of the alkoxy radical Grassie and Scott (1985). In addition to the polymer oxidation initiation by the photolysis of hydroperoxide groups, a second major contributor to the photodegradation of polymers is ketone photolysis, which proceeds through two major reactions called Norrish I (radical generation and no chain cleavage) and Norrish II (chain cleavage), as shown below. Ketones are introduced

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 6 of 32

Figure 2 A plastic item with thirty years of exposure to heat and cold, brake fluid, and sunlight.

onto the backbones of polymers by photooxidation. On exposure to light, these ketone groups absorb photons of appropriate energy, break carbon–carbon bonds, and scission the polymer backbone (Rabek 1995; Feldman 2002) as shown in the Figures 3 and 4 (Grassie and Scott 1985): Propagation step

This step can be divided into Rabek (1987) six different steps: A) Subsequent reaction, of low molecular radicals (R.) and polymer alkyl radical (P.) in a chain process

Figure 3 The β scission in polymer molecule, Grassie and Scott (1985).

similar to the abstraction of hydrogen from the polymer molecule: (7) B) Reactions of polymer macro radicals with oxygen, during which polymer peroxy radicals (POO.) are formed. (8) C) Abstraction of hydrogen from the same or another polymer molecule by polymer alkylperoxy radical, with the formation of a hydroperoxide group.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 7 of 32

Figure 4 Polymer photooxidation, Yousif (2012).

(9) D) Photodecomposition of hydroperoxide groups with the formation of polymer alkyloxy (PO.), polymer peroxy (POO.), and hydroxyl, (HO.) radicals. POOH

PO. + .OH

(10)

2POOH

PO. + POO. + H2O

(11)

E) Abstraction of hydrogen from the same or another polymer molecule by polymer alkyloxy radical with the formation of hydroxyl function groups in polymer.

(12) F) Dispropertionation reaction (scission process) of polymer alkoxy radicals with the formation of aldehyde end groups and end polymer alkyl radicals.

low (ca.1%) Mayo (1978) because of efficient polymer alkyl radicals (P.) recombination before O2 react with them. Polymer alkylperoxy radicals (POO.) are strongly resonance stabilized, and they are stable at room temperature in polymer matrix. They are selective electrophilic species abstracting 3° hydrogen in preference to 2° or 1° (Mill 1978; Guillet 1978 Yousif et al. 2011b). The light quanta produced by sun irradiation are energetically sufficient to cleave PO – OH and also P – OOH , but hardly POO – H bonds , which have the dissociation energies of 42 kcal/mol (PO – OH), 70 K cal/mol (P – OOH) , and 90 kcal/mol. (POO – H) Ranby and Rabek (1975b).The large differences in bond dissociation energy between PO – OH and P – OOH means that reaction with formation PO• and •OH radicals will predominate during light irradiation. The most probable mechanism of photodecomposition of -OOH group occurs through energy transfer processes from the excited carbonyl or aromatic hydrocarbon groups (donors) to hydroperoxy groups (acceptors). (donor)*+ -OOH (acceptor)

(13) There are many points concerning the mentioned propagation steps which are: Formation of propagating radicals (POO.) by

reaction (8), in a semi-rigid polymer system is very

donor + (-OOH) *…

(14) (-OOH)*

-O•+ •OH…

(15)

Generally, the overall processes of photooxidative degradation are given in the Figure 4 Yousif (2012) (Figure 5):

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 8 of 32

Figure 5 Photooxidation cycle for polymers.

Termination step

History of polystyrene

The radicals formed in the degradation of polymers can be terminated by numerous different combination reactions between two polymer radicals, in which inactive products are formed:

Edward Simon accidently discovered polystyrene in 1839 in Germany. From the resin of Turkish sweetgum tree, Liquidambar orientalis he obtained an oily substance, which thickened into jelly in air; he described it as styrol oxide. In 1845 John Blyth and August Wilhelm von Hofmann observed that the same changes occur in styrol in the absence of oxygen. They named it as metastyrol. Marcelin Berthelot in 1866 found that a polymerization process is responsible for the change styrol to metastyrol. In the thesis of Hermann Staudinger (1881–1965) it was reported that a chain reaction occurs in styrol resulting in the formation of macromolecules which was later called polystyrene. In Germany, I. G. Farben, company in 1931 started producing polystyrene in Ludwigshafen. The Koppers Company in Pittsburgh, Pennsylvania produced expanded polystyrene in 1959.

(16) (17) (18)

When the oxygen pressure is high, the termination reaction follows reaction (17) almost fully. At low oxygen pressure other termination reactions take place to some extent. In the degradation of solid polymers when sufficient oxygen content cannot be maintained reaction (18) becomes significant. Polymer radicals can couple mutually as in reaction (19) and form crosslinks with polymer peroxy radicals (Rabek and Ranby 1975; Ruoko, 2012) (Figures 3 and 6). Polystyrene

Polystyrene (PS) is a multipurpose polymer that is used in varied applications in rigid and foamed form. General purpose polystyrene is clear and hard which is used in packaging, laboratory ware, and electronics Meenakshi et al. (2002).

Synthesis of polystyrene

Polystyrene is manufactured by the addition polymerization of the styrene monomer unit. At room temperature, polystyrene is normally a solid thermoplastic, but can be melted at higher temperature for molding or extrusion, then resolidified. Styrene is an aromatic monomer, and polystyrene is an aromatic polymer (Ruoko, 2012). The main manufacturing route to styrene is the direct catalytic dehydrogenation of ethyl benzene as in Figure 7.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 9 of 32

Figure 6 Polymer film before and after exposure to UV light.

The reaction shown above has a heat of reaction of −121 Kj/mol (endothermic). Nearly 65% of all styrene is used to produce polystyrene. The overall reaction describing the styrene polymerization was shown in Figure 8. Polystyrene is produced radical- initiated suspension polymerization. And some is produced by reactive extraction.

Types of polystyrene

On the basis of structure polystyrene can be classified into three forms Figure 6. The polystyrene containing all of the phenyl groups on one side is of the planer zig – zag mechanism termed as isotactic polystyrene. If the phenyl groups are randomly distributed then it is called atactic polystyrene. Radical vinyl polymerization yields atactic polystyrene. The polystyrene containing phenyl groups on alternating sides of the chain is described as syndiotactic polystyrene (sPS), which is highly crystalline. It has the tendency to crystallize very quickly which gives it the favourable properties of high melting temperature and chemical resistance (Saitoh et al. 2003; Gupper and Kazarian 2005) (Figure 9).

Uses of polystyrene

Polystyrene is a type of plastic that is used for a variety of functions including in rigid items such as refrigerator crispers, coat hangers, DVD cases and printer cartridges. One of the important uses of PS is in the manufacture of cover signal lamps of some automobiles Safy Eldin and El-laithy (1994). It is a brittle, high glass transition temperature polymer. Pure solid polystyrene is a colorless, hard plastic with limited flexibility which can be cast into molds with fine detail. Polystyrene is used in numerous plastic products. It is economical and is used for producing plastic model assembly kits, plastic cutlery, Fried (2003) for packaging and in sulation materials in the form of a foam or bead, and in electronics, construction, house and medical ware and disposable food services Meenakshi et al. (2002) and many other objects where a fairly rigid, economical plastic of any of various colors is desired. Polystyrene fabricated into a sheet can be stamped (formed) into economic, disposable cups, glasses, bowls, lids, and other items, especially when high strength, durability, and heat resistance are not essential. A thin layer of transparent polystyrene treditimatly been used as an infrared spectroscopy standard. This is the lightweight

catalyst

CH3 Figure 7 Synthesis of styrene.

CH2

H2 (19)

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 10 of 32

(20)

X CH2

CH2

CH X

Figure 8 Polymerization of styrene.

material of which coffee cups and takeaway food containers are made. The voids filled with trapped air give expanded polystyrene low thermal conductivity. It is also used as insulation in the wall of building. When a polymer matrix is mixed with inorganic nanoparticles, the thermal (Garcia et al. 2009), mechanical (Uhl et al. 2002), optical, electrical, magnetic and flammability properties of such a nanocomposite are much different from the polymer matrix itself Manzi-Nshuti et al. (2009).

long period of time thus cause environmental pollution Singh and Sharma (2008). As waste plastic material has become a serious problem, recycling is receiving attention as a means of preserving the environment and reserving resources Pantano et al. (2009). Polystyrene waste requires the transportation of big large volume of materials, which is costly and makes recycling economically unfeasible.

Degradation of polystyrene Environmental effects of polystyrene

Synthetic plastics are used in many fields such as packing, household, agricultural, marine and architectural. Plastics have replaced natural resources such as cotton, wood and metals because of their light-weight, and durability. PS is a widely used thermoplastic. Its hardness, hydrophobic nature and chemical composition cause it to persist in nature without any decomposition for

Figure 9 Types of polystyrene.

Polymers are weathered due to environmental factors such as light and temperature. The conditions of use play a key role in the degradation of plastics. Polystyrene losses its mechanical and tensile properties due to effect of UV light and heat Kiatkamjornwong et al. (1999). UV light induces the production of radicals by oxidation. Radicals cause the chains of polymer to breakdown.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 11 of 32

Figure 10 World consumption of polystyrene–2010.

Consumption of polystyrene in the world

Polystyrene, a thermoplastic resin that is easily processed has many applications such as disposables, packaging, toys, construction, electronics and houseware. The following pie chart shows world consumption of polystyrene (see Figure 10). Asia is the overall leader in production and consumption of polystyrene, with 53% of total world production and 47% of total consumption of polystyrene in 2010. North America

and Western Europe follow distantly at about 17-19% of the total production and consumption each. Through the recession, the percentage of imports of EPS resin relative to consumption rose from 40% to 44% over 2007 through 2010. Global demand for polystyrene and expandable polystyrene increased from 13 mln tons in 2000 to around 14.9 mln tons in 2010. Packaging, construction, appliances and consumer electronics industries were the major consumers of polystyrene and expandable polystyrene.

Figure 11 FTIR spectra of (a) pure polystyrene and after (b) 30 days and (c) 15 days of degradation, (Pushpadass et al. 2010).

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 12 of 32

Figure 12 Change in UV. Vis. spectram of polystyrene film after irradiation time, Shao et al. (2013).

analyses of photo irradiated polystyrene showed increase in absorption peaks at 1742-1745cm-1 indicating the presence of ketone carbonyl groups. For polymer of hydrocarbon, oxidation must precede biodegradation. Kiatkamjornwong et al. (1999) (see Figures 11 and 12).

The global demand for polystyrene and EPS is rising within developing countries such as China, India, Iran, Saudi Arabia and Brazil. Slovakia’s EPS consumption follows the trend set by other EU countries, whose year-on-year increase in consumption was about 3.3 percent during the monitored period. Of all EU countries, France, Poland, Austria and Germany reported the highest consumption of EPS. The lowest consumption was registered in Greece, Hungary, Italy and Spain. Complete insulation of a building using EPS can achieve a reduction of up to 66 percent in the heat consumption of prefabricated buildings, while in the case of detached family houses this can rise to as much as 70–79 percent. The life span of such insulation is about 50 years.

Photooxidative degradation of polystyrene by radical processes

All commercial organic polymers degrade in air when exposed to sunlight as the energy of sunlight is sufficient to cause the breakdown of polymeric C–C bonds as a consequence of degradation. The resulting smaller fragments do not contribute effectively to the mechanical properties and the polymeric article become brittle. Thus the life of thermoplastics for outdoor applications becomes limited due to weathering Andrady et al. (1998). When polystyrene is subjected to UV irradiation in the presence of air, it undergoes a rapid yellowing and a gradual embrittlement. Industrially, the yellow discoloration is an important adverse effect of the ageing of polystyrene, e.g. during exposure outdoors (Geuskens et al. 1978a, 1978b; Weir 1978; Lucki and Rnby 1979; Rnby and Lucki 1980). Photodegradation and photooxidation of polystyrene film and solutions have been widely investigated (Rabek & Ranby 1974a, 1974b; Lawrence and Weir 1973). The main reactions observed are bond session, chain crosslinking and oxidative degradation. In spite of these great efforts the mode of photodegradation of polystyrene

Photodegradation of polystyrene

Photodegradation of polystyrene in air causes discoloration (yellowing), cross-linking, and chain scission due to oxidation. A photodegradation process was also proposed on the basis of the IR spectrum of the photoirradiated film, which indicated the formation of peroxy radical and hydroperoxide intermediates. The photochemical reactions cause the dissociation of a polystyryl radical by creating an electrochemical excited state. The polystyryl radical is converted to peroxy radicals by reacting with oxygen. The peroxy radical undergoes chain scission and formation of carbonyl compounds. The photosensitivity has been evaluated of plastic sheet after different exposure times (0.5, 5, 10 or 21 hr.). FT-IR CH2

CH2

* + hv

[ ] [ ] 1

ISC

Figure 13 Formation of triplet state after absorption of light by benzene ring in PS.

( 21)

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

H2C

Page 13 of 32

. *

CH2 - CH

( 22 )

Figure 14 Dissociation of C6H5-C bond.

(2) Triplet energy excitation can be transferred by intramolecular energy transfer processes to the C – H or C – C bonds (Figure 15).

is still very controversial. A number of impurities and irregularities in polystyrene, such as hydroperoxides, aromatic carbonyl groups, olefin bonds and chain peroxide linkages, can be responsible for the photoinitiation of the radical oxidation of polystyrene Rabek (1987). Irradiation of polystyrene by UV. and visible light with wavelength (λ< 400) nm., leads to the formation of radicals whose nature is dependent on the spectral composition of the light and irradiation condition Kuzina and Mikhailov (1993). The end group of PS or ketonic impurities also absorb the light of wave lengths longer than 300 nm (Geuskens and David 1979a, 1979b; Klopffer 1975; George and Hodgeman 1977). Absorption of light quanta by benzene rings is the first step producing excitation of the rings at excited singlet states which are transformed by intersystem crossing (ISC) to the triplet sate as Figure 13. The secondary step in the reaction of triplet state of benzene, which occurs by one of the following two modes:

It has been suggested that the most important step in photolysis of polystyrene in the absence of oxygen is the scission of a C – H bond. The electron spin resonance (ESR) spectra obtained during the UV, irradiation of polystyrene (PS) were interpreted as arise from radicals formed in reaction (8) Cozzen and Fox (1969); Grassie and Weir (1965). The hydrogen radicals are very mobile; they can diffuse out from the polymer matrix and then recombine with each other to give molecular hydrogen. The generally accepted theories of oxidation of polymers are based on the radical process for the thermal oxidation of hydrocarbons. This process involves peroxy group formation and it proceeds through the following fundamental steps Ranby and Rabek (1975a): initiation, propagation, radical chain branching and termination. Initiation

(1) Triplet energy of the excited benzene may be give rise to the dissociation of the C6H5 – C bond (Figure 14):

H2C

In each repeating unit of polystyrene there is a phenyl chromophore that shifts the absorption spectrum of PS towards the visible region, up to λ≈260 nm. When PS is

H2C

( 23 )

CH +

CH2

H Figure 15 Formation of C-H and C-C bonds.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 14 of 32

irradiated with UV radiation the phenyl ring is excited, after which the excitation energy is transferred to the nearest C−H bond, resulting in the cleavage of hydrogen and leading to polymer radical formation: (24)

(25) The type of the radicals formed during polystyrene photodegradation depends on the irradiation wavelength Ranby and Rabek (1975). The movement of polymer macromolecules in the solid state is restricted, but radicals can migrate along the polymer chain until they trapped by other radicals or by impurities. When two macro radicals are near to each other cross-linking may occur as in Figure 16. On the other hand, macroradicals may disproportionate leading to chain scission (Figure 17). When an end group radical is formed, unzipping may occur with the formation of monomer see Figure 18. During UV irradiation PS samples show increased optical density and slight yellowing. This coloration of PS has been attributed. Grassie and Weir (1965) to the build -UP of conjugated bond sequences in the polymer backbone (Figure 19). Propagation reaction

Polystyrene alkyl radicals (R.) can easily react with molecular oxygen (triplet state), to produce peroxy radicals by addition (Figure 20). Baloglu and Fisch (1994). A polymer peroxy radical can react with the surrounding polystyrene molecule and abstract hydrogen atom see Figure 21.

H 2C

On exposure to light the polymer hydroperoxides can decompose according to the following reactions as shown in Figure 22. Alkoxy polymer radicals produced during the photolysis of hydroperoxide groups may decompose by β-scission reaction and to form a cetophenone and chain aliphatic ketone (Figure 23) (Kuzina and Mikhailov 1998; Geuskens et al. 1978a, 1978b). The general process for photodegradation of polystyrene was shown in Figure 24, (Yousif et al., 2011a). Photostabilization mechanisms in polymers

It is well known that all commonly used plastics degrade under the influence of sunlight. Almost all synthetic polymers require stabilization against the adverse effects; with the development of synthetic resins it became necessary to find ways and means to prevent, or at least reduce, the damage caused by the environmental parameters such as light, air and heat. That is why the photostability of polymers is one of the most important considerations for application. Photostability can be achieved through the addition of special chemicals, light stabilizers or UV stabilizers, that have to be adjusted to the nature of the resin and the specific application considered. The photostabilization of polymers involves the retardation or elimination of photochemical process in polymers and plastics that occur during irradiation. There are several different methods of photostabilization, and the choice of method is dependent on the polymer and application. The most important methods of photostabilization are the screening or absorbing of UV radiation by stabilizing agents and the use of antioxidants, which react with the polymer radicals, stopping the degradation process by forming inactive products (Ruoko 2012; Yousif et al. 2011a, 2011b).

. .

H 2C

(26)

Figure 16 Formation of cross-linking when two macroradical are near.

C H2

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 15 of 32

H2 C

CH2

(27)

+ Figure 17 Macroradical disproportionate.

The following stabilizing systems have been developed which depend on the action of stabilizer: (a) light screeners, (b) UV absorbers, (c) excited state quenchers, (d) peroxide decomposers and (e) radical scavengers. Of these, it is generally believed that types c, d and e are the most effective Yousif et al. (2011a, 2011b). Practice shows that when the polymer contains a photostabilizer, the oxidation rate is much reduced. Stabilizers reduce but do not completely prevent oxidation, so it can be expected that some reaction will take place in the interior of a stabilized polymer.

Ultraviolet Stabilizers

Ultraviolet Stabilizers additives for plastics and other polymer materials which prevent the photodegradation or photocrosslinking caused by ultraviolet light. The UV absorber and screener operate by absorbing the incident UV radiation preventing it from reaching the bulk of the polymer and converting the energy thus acquired into a less damaging form such as heat or they may act as radiation reflecting or scattering (preferably coating) Decker and Biry (1996) on the surface of the polymer thus delaying discoloration and delamination. An important disadvantage of UV absorbers is the fact that they need a certain absorption depth (item thickness) to provide good protection to a polymer. Therefore, the protection of polymer surfaces and of thin items such as films or fibers is only moderate Gugumus (1987). The amount of an absorber required to provide economical protection in a plastic is governed by several factors such as: H2 C

H2C CH

i. Thickness of the plastic. ii. Tolerance of color. iii. Effect of high concentration of absorber in plastics. iv. Compatibility of the absorber in the plastic. The most common UV stabilizers are: UV absorber and light screeners, quenchers, hydroperoxide decomposers, radical scavengers and singlet oxygen, (1O2). Ultraviolet stabilizers can be classified according to their mechanisms of action in the photostabilization process into: (i) UV absorber and light screeners. (ii) Quenchers. (iii) Hydroperoxide decomposers. (iv) Radical scavengers. (v) Singlet oxygen, (1O2), quenchers. The UV stabilizer can be classified into: Rabek (1987)

(i) Pigments. (ii) Metal chelates. (iii) Carbon black. (iv) Salicylates. (v) Salicylanilides. (vi) Hydroxy phenyl benzotriazoles. (vii) Hydroxy benzophenones. Mode of action of UV. Absorber

The action of UV absorber is relatively simple, it interact with the first step of the photooxidation process, that is, it absorbs the harmful UV radiation before it reaches to

H2C

Figure 18 Formation of Styrene monomer.

. ( 28 )

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

H2C

Page 16 of 32

H2C

CH HC

H2C

CH HC

+H2

. + H

( 29 )

Figure 19 Built up of conjugated bond sequences in the polybachbone.

the photo active chromophoric species in the polymer molecule (300–400) nm. Thus the energy dissipates in a manner that does not lead to photosensitization. A UV absorber must be light stable, because otherwise it would be destroyed in stabilizing reactions. Certain phenolic and non-phenolic UV absorbers with structures (1), (2), (3) and (4) respectively, display high performance and inherent photostability in the (300–400) nm. region required for protection of polymers against photodegradation .The structure of some UV absorbers are shown in Figure 6: Pospisil and Nespurek (2000). Hydroxy benzophenones and hydroxyphenyl bezotriazoles are the most extensively studied UV absorbers Gugumus (1979) (see Figure 25). Generally, after photons are absorbed by the chromophores, molecules rise to higher excited state, by spin inversion of singlet state. The singlet states may change to triplet state by intersystem crossing (ISC) or return to a lower excited state by internal conversion (IC) (these are radiationless processes). Excited states have the ability to lose the excitation energy by some radiation processes such as fluorescence or phosphorescence or by energy transfer to another molecule. Concerning the energy transformation in hydroxy benzophenones, it has been shown with 2-hydroxy benzophenone (Gugumus 1979; Allen 1983), that on exposure to light, it is transformed into the enol form which turns back into its initial form on losing thermal energy to the medium. On the basis of spectroscopic data, it is concluded that the energy transformation involves exclusively a fast radiationless transition.The

photostabilizing process of O-hydroxy benzophenone has been the subject of many investigations Collell & Amer (1968). The most probable process involved is the utilization of the energy of the absorbed photon to intramolecular proton transfer during which a quinone structure is formed. An O-hydroxyphenone molecule in the ground state (S0) absorbs a photon as is excited to the singlet state (S1) (as in Figure 26), Yousif (2012). In this excited singlet state (S1) the proton of a hydroxyl group is transferred to the carbonyl group during which a quinone structure is formed (Figure 27). The excited singlet sate (S1) of the quinone structure is converted by intersystem crossing (ISC) to the excited triplet state (T1) (Figure 28). Since in the excited triplet state (T1), the stable structure is the ketone structure, see Figure 29. The intersystem crossing (ISC) process leads from the excited triplet sate (T1) of the ketone structure directly to the ground state (S0) (Figure 30). It has been shown that urethane and silylated derivatives of hydroxybenzophenones are effective photostabilizers, but cannot photostabilize polymers by intramolecular proton transfer Olson and Schroeter (1978). These compounds can act as: (Senna et al. 2002; Pospisil et al. 2002; Patel, 2007). (i) Light screeners. (ii) Excited state quenchers of chromophoric groups present in polymers. (iii) Radical scavengers.

O H2C C

H2 C

H2C C

+ O2

Figure 20 Producing peroxy radical.

H2 C CH

(30)

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

O O H2C

Page 17 of 32

H2 C

H2C CH

OOH H 2 C

H 2C

+ H2C C

(31)

H2 C CH

Figure 21 Polymer peroxy radical abstracted hydrogen.

(iv) Hydroperoxide decomposers. The photostabilizing effect of many aromatic compounds to be UV stabilizer for several polymers has been reported. This is due to their filtrating action which depends in turn, on their absorption characteristics (Ranby and Rabek 1975; Heller 1969).

Pigments

Pigments are insoluble inorganic or mineral and organic compounds of complex structure, such as:

Powder metal (aluminum) is excellent reflector to UV light. Fe2O3, Fe3O4, ZnO,TiO2… are inorganic pigment excellent UV screener. Organic pigments such as azo and anthraquenone display good UV light absorption. Pigments used as additives, are incorporated into polymers, coating, inks, etc.…. for: (i) Cost reduction. (ii) Reinforcement. (iii) Hardening.

O H 2C

OOH H 2 C C

H2 C

H2 C CH

+ OH

(32)

H 2C C

H2 C CH

+ OOH

Figure 22 Decomposition of hydroperoxide.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

O H 2C

Page 18 of 32

. H2 C

O HC

H2 C

CH2

( 33 )

H2 C CH

H2 C

O C

H2 C CH

. +

Figure 23 Formation of alkoxy polymer radicals.

(iv) Improving slip and skid resistance. (v) Color effect. (vi) Storage stability. A pigment as a light screener should be

(i) Light stable for long term performance without fading. (ii) Heat stable to withstand polymer processing conditions. (iii) Migration resistant. (iv) Low cost and non-toxic. The influence of pigments in polymer photostability is not completely understood. If an absorbing pigment is introduced into a polymer, it acts as an inner screen for photo products. If these products are not photooxidized, they accumulate in the polymer matrix. Since pigments act as highly absorbing additives, photooxidative phenomena will be limited mainly to the surface of samples Yousif (2012); Yousif (2010).

such as polyethylene. Their high efficiency as light stabilizers is probably due to their ability to act as inner filters for UV radiation, and as radical scavengers, because many of the carbon blacks contain stable radicals Szwarc (1956), and quenchers of singlet and triplet states of polymers. The effectiveness of carbon blacks is dependent upon Williams et al. (1969) the type of carbon black, the particle size and the degree of dispersion in the polymer phase. Thus the UV stabilization efficiency of carbon black increases as the particle size decrease. An optimum concentration of carbon black is 3-5%. Higher than this concentration, the polymer looses it tensile strength and other mechanical properties David and Hsuan (2003). Quenchers

Quenchers deactivate excited states (singlet and/or triplet) of chromophoric groups in polymers before bond scission can occur by two mechanisms (Wiles 1979; Wiles and Carlsson 1980). 1. Energy transfer process. 2. Chemical and/or physical deactivation.

Carbon black

Carbon black is one of the most efficient and widespread light absorbers. It consists of very fine particles fused together to form primary aggregates. The micro structure of carbon black particles is illustrated in Figure 31, David and Hsuan (2003). Carbon black contains different functional groups such as carbonyl, hydroxyl, quinone, ether, etc.… Carbon black absorbs UV radiation more efficiently than conventional colored pigments, carbon black are efficient light stabilizers for polymers Winslow et al. (1969)

The excited state of a chromophore (Ch) {where Ch is a chromophore such as dyes, pigments, antioxidant products, carbonyl groups, a variety of impurities or pollutants such as polynuclear aromatic compounds} may react but it can also be made to transfer its excess electronic energy to a quenching entity (Q) (see Figure 32). If energy transfer to the quencher can compete with reaction, decomposition… etc. by Ch, and if Q can dissipate the excess energy harmlessly, then the system is stabilized. Energy transfer can occur efficiently only if the

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 19 of 32

Figure 24 General mechanism of photodegradation of polystyrene, Yousif et al. (2011a, 2011b).

energy level of the quencher is below that of the chromophore Lamolla (1969). Quenching of electronically excited states (singlets or triplets) is frequently described in terms of two distinct phenomena: (i) Long range energy transfer, e.g., a dipole/dipole interaction as is considered to operate between the chromophore and quencher even at distaices >50A if there is significant overlap between the emission spectrum of Ch and the absorption spectrum of Q Lamolla (1969).

(ii) Contact (collisional) energy transfer of various kinds is said to require that Ch* and Q be within 10 to 15. In practice, the quenching of excited triplets is usually ascribed to collisional transfer (Beavan and Phillips 1974; Dan et al. 1973). In the solid state, transfer of energy occurs by conjugative or dipole-dipole interactions. The photooxidative degradation is promoted by the electronically excited oxygen molecule (singlet oxygen 1O2) formed in polymers. The [1O2] can also be generated in polymers by energy transfer

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 20 of 32

OH N

subst C

N H

subst

2 subst

O NH C C NH

CH NH

Figure 25 Examples of UV absorbers.

O C

(34) S1

Figure 26 O- hydroxybenzophenone absorbed a photon.

H OH

O C

(35) S1

S1 Figure 27 Formation of Quinone.

H O

O C

ISC S1

* (36)

Figure 28 Formation of excited triplate state of O- hydroxybenzophenone.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 21 of 32

H O

(37) T1

Figure 29 Stable structure of excited triplate state of O- hydroxybenzophenone.

O C

ISC

( 38 ) S0

Figure 30 Formation of singlate excited state of O- hydroxybenzophenone.

Figure 31 The micro structure of carbon black particles, (Chirinos 1989).

reaction

+ Q

Ch Q

product Figure 32 General processes for Quenchers.

+ heat

(39)

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 22 of 32

COOH

CH3

HO O

POOH

+ Ni (NO3)2 + 2POCH3

hv C

CH3

(1.41)

O OH

Figure 33 Example of hydroperoxide decomposer.

(2)

hv+O2+R

(1.42)

(1)

OR (3)

ROO

Figure 34 The general cycle for protecting a polymer against degradation by HALS, Willis (1984).

CH3

N O

Si n

H 2C CH2 O CH2

O (CH2) 8 C

O N

H Uvasil992 N

H Tinouvin770 Figure 35 The chemical structures of HALS, Bottino et al. (2004).

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Figure 36 Theory of antioxidant.

Figure 37 Quinones retard oxidation process.

Figure 38 Light stabilize function.

Page 23 of 32

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 24 of 32

S O

S S N

Where M= Sn (II), Cd(II), Ni (II)M Zn (II), Cu (II)

Figure 39 Structure of 2-thioacitic acid benzothiazol complexes.

Nickel chelates can photostabilize a polymer by one or more of the following mechanisms.

from electronically excited carbonyl group to dissolved molecular oxygen Heskins and Guillet (1968). The quenching of [1O2] is also necessary for effective stabilization. Nickel chelates have been proven to be very effective quenchers for the excited state of [1O2] Schmitt and Hirt (1963).

(i) Quenching of the excited state of carbonyl groups (ketones) through energy transfer. (ii) Quenching of the singlet oxygen (1O2) Allen et al. (1984). (iii) Decomposion of the hydroperoxides (OOH) radical, to non radical inactive species Yousif (2010). (iv) Scavenging of radicals (alkylperoxy (ROO.) and alkyloxy (RO.) Allen et al. (1982).

Energy transfer

Energy transfer in a polymer is very important as this transfer is directly related to the effects of photostabilization and photodegradation Guillet (1972a, 1972b). The energy transfer in polymers can occur by one of the following processes:

Hydroperoxide decomposer

These compounds operate by reacting directly with polymeric hydroperoxide (ROOH). The decomposition of hydroperoxide in polymer to non radical derivatives was first demonstrated Carlsson and Wiles (1974). Many metal complexes of sulphur containing ligands such as dialkylthiocarbonate and dialkylthiophosphate not only decompose hydroxide in PE film but are also effective in UV stabilization (as UV absorbers and excited state quencher). Generally there are three groups of compounds which operate by quite distinct process Aliwi (2001). Compounds that belong to this type are organic phosphites and some Nickel chelates. They function by reducing hydroperoxide stochiometrically as presented in the Figure 33.

(i) Intermolecular energy transfer This process may occur between an excited polymer molecule (donor) and the molecule of a photostabilizer (acceptor) or between an excited sensitizer (donor) and a polymer molecule (acceptor). (ii) Intramolecular energy transfer This process occurs within same polymer molecule, e.g. between an excited chromophore in the chain (donor) and another segment of the polymer molecule (acceptor). This process is especially interesting in co-polymers. Guillet (1972a, 1972b). Nickel chelates are very effective quenchers of the triplet state of carbonyl groups in polyolefins. These chelates have been tested for photostabilization of polyisobutylene, poly butadiene Lala and Rabek (1980), polystyrene George (1974), PVC, poly (2,6-dimethyl-1,4-phenyloxide) and poly urethanes. (Chandra 1983; Osawa et al. 1979).

Hindered amine peroxide decomposer

Hindered amine light stabilizers (HALS) have been found to be remarkably effective in performing both radical trapping and hydroperoxide decomposition.

* N

hv S

+ heat S

Figure 40 Suggested process for photostabilization by benzothiazole as UV absorber, Yousif et al. (2012).

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 25 of 32

O S O H 2C

CH2

S OH H2C

OOP

CH2

Figure 41 Suggested process for photostabilization by benzothiazole complexes as peroxide decomposer, (Yousif et al. 2012).

from (HALS), is prone to scavenge alkyl and form O-alkylhydroxylamines Bagheri et al. (1982). Therefore HALS of different structure are able to interconvert in cyclic pathways, destroying species which could lead to polymer degradation and coating species which protect the polymer against degradation Willis (1984). It has been generally accepted that hindered piperidine (e.g., 2,2,6,6- tetramethyl piperidine, which is the simplest

These are one of the most effective photostabilizers for polymers and have been used in a large number of commercial polymers. They are efficient and cost-effective in many applications, despite their high prices Willis (1984). The mechanism of (HALS) activity includes scavenging of R., ROO and deactivation of hydroperoxides (ROOH) and peracids, which are based on a complex of chemical transformations. Nitroxide the key intermediate formed

S O S

H 2C

M O

S C

CH2

POO

S H

POO S

H 2C

M O

S C

CH2

S H

POO S

H2C S

M O

S C

CH2

Figure 42 Suggested mode for photostabilization by carboxylate complexes as radical scavengers.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 26 of 32

H3C HO

CH3 C

CH3

N N N

CH3 C

Tinuvine 327

2-hydroxy-4-methoxybenzophenone

CH3

H3C

Figure 43 Structures of 2-hydroxy-4-methoxybenzophenone and Tinuvin 327.

model compound for HALS), during UV irradiation in the presence of oxygen (air) and radicals (R.), produces hindered piperidinoxy radicals according to the reaction 1 Yousif et al. (2011b): Piperindoxy radicals react with alkyl radicals (R.) to give a substituted hydroxypiperidine as shown in reaction 2 in Figure 34. For the reaction of nitroxyl with (POOH) precedes via the formation of an intermediate (hydroxylamine) which reacts with (PO.) to generate the nitroxyl as reaction 3 as in Figure 31; Kurumoda et al. (1985). Recently, different types of hindered amine light stabilizer have been synthesized to improve the compatibility of the additive with the polymer and enhance the long term of retention during the aging of polystyrene. HALS reduces the photooxidation by acting as radical scavengers. HALS structures are shown in the Figure 35 Bottino et al. (2004).

Radical scavengers

The scavenging of radical intermediates is another possibility for polymer stabilization, analogous to that used in

thermal degradation. Quinones react with alkyl radicals to form radicals that do not initiate polymer oxidation. The radicals scavengers operate by interfering with the propagating step in the oxidative chain and this can be achieved by two routes: (i) Reaction with propagating radicals (P., PO. POO.). (ii) Reaction with resulting hydroperoxides which are the source of chain branching through the propagating process (Feldman 2002). Antioxidant

The development of the auto-oxidation theory, in which the propagating radicals, alkyl, alkylperoxy (R.,ROO.) and the hydroperoxide (ROOH) are the key intermediates, has led to a comprehensive theory of antioxidant action. The two major anti-oxidant mechanisms are shown in Figure 36. The chain breaking donor (CB-D) and chain breaking acceptor (CB-A). Also an anti-oxidant can act by a preventive inhibition processes. Many reducing agents e.g. hindered phenols and aromatic amines, which reduce the ROO. to

N N OH

hydroxyl phenyl pyrazole Figure 44 Structure of hydroxyl phenyl pyrazole.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 27 of 32

OC6H13

N N

hydroxyphenyltriazine

Tinuvin 1577

Figure 45 Structures of Tinuvin 1577 and hydroxyphenyltriazine.

hydroperoxide in CB-D step have already been empirically selected and used for rubbers and by this time also for the newer plastics industry Cheremision (1997). Oxidizing agents, e.g. quinones which have been shown to be able to retard oxidation, can function as antioxidants (via a chain breaking acceptor process), if they can compete with oxygen for alkyl radicals Watson (1953), as shown in the following equation see Figure 37. Hydroperoxides (ROOH) are the primary molecular photooxidation products and the most dangerous

chromophore in the photodegradation of polymers. Their deactivation by a hydroperoxide decomposing antioxidant (HDAO) or hindered amine stabilizer (HAS) reduces ROOH hom*olysis and consequently, chain initiation and transfer. The general light stabilizer function was shown in Figure 38. Photostabilization of polystyrene

The photostabilization process may be accomplished with commercial light stabilizers in addition to chalate O

O HN HN N H

S O

N H

NH2

6 aminothiouracil

6 aminouracil

O H3C N

H 3C S

N H

NH2

6 amino-s-methyluracil

N CH3

1,3-dimrthyluracil Figure 46 Structures of uracil derivatives.

NH2

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 28 of 32

complexes. The nature of the photostabilizer and polymer will determined the process and efficiency of photoprotection of the polymer film. The route by which photodegradation occurs and the importance of the impurities remaining after either polymerization or processing have to be known to determine the most satisfactory method of stabilization George (1974). Complexes of 2-thioacitic acid benzothiazol have been used as additives to increase the photostabilization of polystyrene. The structures of these additives as shown in Figures 39, 40, 41, 42. Two methods have been used to monitor the extent of photodegradation of polystyrene films. The first was by using FTIR spectra. The progress of photodegradation at different irradiation times was followed by observing the changes in carbonyl and hydroxyl peak intensities. Then, carbonyl (ICO) and hydroxyl (IOH) indices were calculated by comparison of the intensities of absorption peaks at 1720 and 3450 cm-1 with that of a reference peak at 1450 cm-1. This is called band index method. The second method involves measuring the average molecular weight using viscometry technique. These additives stabilize PS film through UV absorption or screening, and by peroxide decomposers, or radical scavengers Yousif et al. (2012). The photochemical and photophysical protection for polystyrene by commercial UV absorbers such as 2-hydroxy-4-methoxybenzophenone and Tinuvin 327 involves triplet energy transfer from excited polymer carbonyl impurities groups in addition to UV screening George

(1974). The structures of these compounds are shown in Figure 43. Other categories of UV absorbers (hydroxyl phenyl pyrazole) have been shown to be able to act as photostabilizers to prevent oxidation or degradation of polystyrene. They may behave as an efficient triplet state quencher of carbonyl impurities in the polymer mainchain. Sastre et al. (1991) (see Figure 44). Many commercial light stabilizers have been developed in an attempt to overcome the problem of photodegeradation of PS articles. The presence of various concentrations of Tinuvin 1577 Bottino et al. (1996), thiadiazole compounds Yousif et al. (2011a) and hydroxyphenyltriazine, additive effectively inhibits the surface photooxidation of PS Bottino et al. (1999). Also a new family of UV absorbers; the dihydroxyphenylpyrazoles, has shown to be effective as photostabilizers as they effectively prevent the photoxidative degradation of PS films Sastre et al.( 2003). The compounds structures are shown in Figure 45. Uracil derivatives have been used as photostabilizers for PS. The results reveal a higher stabilizing efficiency for the materials investigated relative to the two commercial UV absorbers, phenyl salicylate and 2-hydroxybenzophenone derivative Rabie et al. (2008). The structures of uracil derivatives was shown in Figure 46. The photooxidation of PS decreased with addition of high molecular weight of HALS (linear peroxide amine type of new polymeric HALS) and the photostabilization efficiency was similar or better than that of Cyabsorb 3529 Sun et al. (2002) (Figure 47).

N N N

(CH2)6

n O

Cyabsorb UV 3529 Figure 47 Structure of Cyabsorb UV 3529.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Page 29 of 32

H O

M HO

O H

H2 N

M HO

N H2

M=Cu , X=Cl M=Vo , X=SO4 M=Ni , X=(CH3COO)2

Figure 48 Structure of anthraquinone derivatives.

Ar O O

N N

SH O

O Figure 49 Structure of 2,3dihydro-(5-mercapto-1,3,4-oxadiazol-2-yl)-phenyl-2-(substituted)-oxazepine- 4,7-dione.

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Photostabilization of PS films by anthraquinone derivatives and their complexes with copper(II), oxovanadium (IV) and nickel(II) ions has also been studied as shown in Figure 48 Abd et al. (2009). Four methods have been used to monitor the degradation of polystyrene. There are: FTIR spectroscopy (measuring carbonyl and hydroxyl indexes), UV- visible spectroscopy, and solution viscosity (molecular weight). The last method for identification of degradation is by weight loss. The two anthraquinone derivatives and complexes provide good stabilization. Nickel and copper complexes provide better resistance to degradation than the uncomplexed anthraquinones Abd et al. (2009). The photostabilizing effect of 2,3 dihydro-(5mercapto-1,3,4-oxadiazol-2-yl)-phenyl-2-(substituted)oxazepine- 4,7-dione compounds in PS has been reported. These additives stabilize PS films through UV absorption or screening, peroxide decomposition and radical scavenging Yousif et al. (2013) (see Figure 49). The protection of polystyrene films by UV absorbers including Ni(II) chelate complexes has been studied. Acetylactonate of Ni(II), Cu(II), and Co (III) complexes are more efficient than the corresponding Fe(III) complex for the photostabilization of PS. George (1974); Aliwi et al. (2001).

Conclusion In recent years, the use of polymeric materials has rapidly increased but it is well established that rapid photodegradation of these materials is possible when they are exposed to natural weathering. This review was talk about the photodegradation and photostabilization of polymers and especially in polystyrene. The “hydroperoxide” (POOH) is the most important initiator in the photooxidative process. So most of the common polymers used in such applications contain photostabilizers to reduce photodamage and to ensure acceptable life times under outdoor exposure conditions. The photostabilization of polymers may be achieved in many ways. The following stabilizing systems have been developed, which depend on the action of stabilizer: light screeners, UV absorbers, excited-state quenchers, peroxide decomposers, and radical scavengers; of these, it is generally believed that excited-state quenchers, peroxide decomposers, and radical scavengers are the most effective. However photoproduction will be enhanced if the additives can decompose –OOH, and possibly act as quenchers of some exited state in the early stages of the photodegradation Competing interests The authors declare that they have no competing interests.

Page 30 of 32

Authors’ contributions EY and RH researched data and wrote the article. Both authors read and approved the final manuscript. Acknowledgment The authors acknowledge the Department of Chemistry, College of Science, Al-Nahrain University for their encouragement. Received: 23 May 2013 Accepted: 29 July 2013 Published: 23 August 2013 References Abd MA, Abdul Zahra AAI, Shenta AA (2009) Photostabilization of polystyrene films by anthraquinones derivatives and their complexes with copper (II), oxovanadium (IV) and nickel (II) ions. Journal of Basrah Researches 35(3):81–97 Aliwi SM (2001) Photostabilization of low density polyethylene for green house application. Nat J chem 2:280–302 Aliwi SM, AL-Ani RR, Awad DAJ (2001) Photostabilization of polystyrene films by Nickel and Copper tetradentate Shiff base complexes. Iraqi journal polymer 5(1):15–30 Allen NS (1983) Photostabilising action of ortho-hydroxy aromatic compounds: A critical review. Polymer Photochemistry 3:167–187 Allen NS, Chirinos-Padron A, Apployarat JH (1982) Photo stabilization of PVC films by using some novel tetra Schiff's bases derived from1,2,4,5-tetra-[5-amino1,3,4-thiadiazole-2-yl]-benzene. Polymer Degradation Stabilization 4:223–228 Allen NS, Chirinos-Padron A, Appleyard JH (1984) Polymer photodegradation: mechanisms and experimental methods. Polymer Degradation Stabilization 6:31–37 Amin MU, Scott G, Tillekeratne LMK (1975) Mechanism of the photo initiation process in polyethylene. Europ Polym journal 11:85–126 Andrady AL (1997) Advance Polymer Science 128:49–94 Andrady A, Hamid S, Hu X, Torikai A (1998) Effects of increased solar ultraviolet radiation on materials. Journal of Photochemistry and Photobiology B-Biology 46:96–103 Ayako T, Hirose H (1999) Advance Polymer Science. Polymer Degradation Stabilization 63:441 Bagheri R, Chakraborty KB, Scott G (1982) Mechanisms of antioxidant action: behaviour of a hindered piperidine and related oxidation products during processing and photooxidation of polypropylene. Polymer Degradation Stabilization 4:1–9 Baloglu R, Fisch M (1994) Polymer Degradation Stabilization 45:30–35 Beavan SW, Phillips D (1974) Photostabilizing of macromolecule by excited state qyencher. Journal Photochem 3:3149363 Blaga A (1980) In: Sereda PJ, Litvin GG (eds) Durability of Building Materials and Compounds, ASTM STP 691. ASTM, Philadelphia, pp 827–837 Bojinov VB, Grabchev IK (2005) Novel functionalized 2-(2-hydroxyphenyl)benzotriazole-benzo[de]isoquinoline-1,3-dione fluorescent UV absorbers: Synthesis and photostabilizing efficiency. Polym Photochem Photobiol 172:308–315 Bottino FA, Di Pasquale G, Pollicino A, Recca A (1996) Surface photostabilization of polystyrene by Tinuvin 1577. Journal of applied polymer science 69:1251–1256 Bottino FA, Bottino G d P, Antonino P, Antonino R (1999) Surface photostabilization of polystyrene by Tinuvin 1577. J of Appl Polym Sci 69(6):1251–1256 Bottino FA, Cinquegrani AR, Di Pasquale G, Leonardi L, Pollicino A (2003) Chemical modification, mechanical properties and surface photooxidation of films of polystyrene. polymer testing. 12:405–411 Bottino FA, Cinquegrani AR, Giovanna DD, Leonardi L, Antnino PA (2004) Study on chemical modification, mechanical properties and surface photooxidation of films of polystyrene stabilized by hinderd amines (HAS), polymer testing. 23:779–789 Carlsson J, Wiles DW (1974) Physical properties of polymers handbook. J polym Sci, polym ChemEd 12:2214–2217 Carlsson DJ, Garton A, Wiles DM (1976) Macromolecules 9:695–701 Chandra R (1983) Photostabilization of poly(2,6-dimethyl-1,4-phenylene oxide) by nickel(II)thiopicoline anilide. Polym Photochem 3:367–378 Cheremision NP (1997) Hand Book of Engineering Polymeric Materials, chapter 8. , New York

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Chirinos AJ (1989) Mechanistic aspects of polymer photostabilization, j. photochem. Photobio A:Chem 49:1–39 Collell E, Amer J (1968) Physiological and pathophysiological aspects of ceramide. J Chem Soc 90:1012–1019 Cozzen RF, Fox RB (1969) 12th Informal Conference on Photochemistry: proceedings of the 12th Informal. J Chem Phys 50:1532–1540 Dan E, Somersall AC, Guillet JE (1973) Macromolecules, New York. 6:228–230 David SL, Hsuan YG (2003) Assessing the photodegradation of geosynthetics by outdoor exposure and laboratory weatherometer. Geotextiles and Geomembranes 21:111–122 Decker C, Biry S (1996) Light stabilization of polymers by radiation cured acrylic coatings. Prog, Org coat 29:81–87 Dindar B, Icli S (2001) Unusual photo reactivity of zinc oxide irradiated by concentrated sunlight. J Photochemistry Photobio A: Chem 140:263 Feldman D (2002) Polymer weathering: photo-oxidation. Journal of polymer and the environmental 10:163–173 Fried JR (2003) Polymer science and technology, 2nd edn. Publishing as Prentice Hall Professional Technical Reference.p, New Jersey, Pearson Education, Inc, 359 Galdi A, Foltis P, Shah A (2010) UV protecting composition and methods of use. US patent, Application, pp 2010–118415 Garcıa N, Hoyos M, Guzman J, Tiemblo P (2009) Comparing the effect of nanofillers as thermal stabilizers in low density polyethylene. Polymer Degrad Stab 94:39–48 Gardella JA (1988) Characterization techniques for polymer blends. Appl Surf Sci 31:72–102 George GA (1974) Mechanism of photoprotection of polystyrene film by some ultraviolet absorbers. J Appl Poly Sci 18:117–124 George GA, Hodgeman DKC (1977) Polymer photodegradation: mechanisms and experimental methods. Eur polym J 13:63–71 Geuskens G, David C (1975) Degradation and Stabilization of Polymers. Halsted, Wiley, New York, pp 113–127 Geuskens G, David C (1979a) Photooxidation of polymers a comparison with low molecular Wight compounds. Pure & Appi Chem 51:233–240 Geuskens G, David C (1979b) Polymer photodegradation: mechanisms and experimental methods. Pure Appl Chem 51:233–240 Geuskens G, Baeyens-Volant D, Delaunois G, Lu-Vinh Q, Piret W, David C (1978a) Polymer photodegradation: mechanisms and experimental methods. J Europ Polym 14:299–303 Geuskens G, Baeyyens-Volant D, Delaunois G, Lu-Vinh Q, Piret W, David C (1978b) Vacuum-ultraviolet photochemically initiated modification of polystyrene surfaces: morphological changes and mechanistic investigations. J Eur Polym 14:291–297 Gijsman P, Diepens M (2009) Photolysis and photooxidation in engineering plastics, Polymer Degradation and Performance. ACS Symp Ser 1004:287–306 Goldshtein J, Margel S (2011) Synthesis and characterization of polystyrene/2(5-chloro-2Hbenzotriazole-2-yl)-6-(1,1-dimethylethyl)-4-methyl-phenol composite microspheres of narrow size distribution for UV irradiation protection. Colloid Polym Sci 289:1863–1874 Grassie N, Scott G (1985) Polymer Degradation and Stabilization. Cambridge University Press, London Grassie N, Weir NA (1965) Polymer photodegradation: mechanisms and experimental methods. J Appl Polym Sci 9:975–981 Guaita M, Chiantore O, Costa L (1985) Changes in degree of polymerization in the thermal degradation of polystyrene. Polymer Degradation stabilization 12(4):135–332 Gugumus F (1979) In: Scott G (ed) Development in Polymer Stabilization-1. Applied Science Publishers Ltd, London, p 261 Gugumus F, Gachter R, Muller H (eds) (1987) Plastics Additives, 2nd edn. Hanser, Munich, pp 97–185 Guillet JE (1972a) Thermal characterization of polymeric materials. Polym Prepr Amer Chem Soc, Div Polym Chem 13:628–632 Guillet JE (1972b) Polymer photodegradation: mechanisms and experimental methods. Pure and ppl Chem 30:135–144 Guillet J (1985) Polymer Photophysics and Photochemistry. Cambridge University Press Guillet TE, Ng HC (1978) Macromolecules, Studies of the mechanism of polyolefin phorodegradation. Pure & Appi Chera 11:929–935 Gupper A, Kazarian SG (2005) Study of solvent diffusion and solvent induced crystallization syndiotactic polystyrene using FTIR spectroscopy and imaging macromolecules. 38(6):2327–2332

Page 31 of 32

Hamid SH (2000) Handbook of Polymer Degradation. Marcel Dekker Inc, New York Heller HJ (1969) Photochemistry of dyed and pigmented polymers. Eurp Polymer J Supplement:99–105 Heskins M, Guillet JE (1968) Polymer photodegradation: mechanisms and experimental methods. Macromolecules 1:97 Kaczmarek H, Kaminska A, Swiatek M, Sanyal S (1999) Photoinition degradation of PS in the presence of low molecular organic compounds. European polymer Journal 36:1167–1173 Kiatkamjornwong S, Sonsuk M, Wittayapichet S, Prasassarakich P, Vejjanukroh P (1999) Degradation of styrene-g-cassava starch filled polystyrene plastics. Polym Degrad Stab 66:323 Klopffer W (1975) Polymer photodegradation: mechanisms and experimental methods. Eurpolym J 11:203 Kochi JK, Wiley J (1973) Handbook of Free Radical Initiators. J A Howard in Free Radicals 2:3 Kurumoda T, Ohsawa H, Oda O, Fujita T, Toda T, Yoshioka T (1985) Entropy and enthalpy effects of 4-(phenylthio)-substituted phenols. J Polymer Science Polymer Chemtry Ed 23:1477–1482 Kuzina SI, Mikhailov AI (1993) Plastics and the environment. Eur Polym J 29(12):1549–1589 Kuzina SI, Mikhailov A (1998) Photocatalytic degradation of polystyrene plastic under fluorescent light. Eur Polym J 34:291–320 Lala D, Rabek J (1980) Polymer photodegradation: mechanisms and experimental methods. Polymer Degradation Stabilization 3:383–391 Lamolla AA (1969) Energy Transfer and Organic Photochemistry, chapter 2. In: Lamolla AA, Turro NJ (eds) Technique of Organic Chemistry. Wiley, New York Lawrence JB, Weir NA (1973) Polymer photodegradation: mechanisms and experimental methods. J Polym Sci Al 11:105–431 Lucki J, Rnby B (1979) Polymer degradation and stability. Pure Appi Chem 1:1–6 Manzi-Nshuti C, Chen D, Su S, Wilkie CA (2009) Structure–property relationships of new polystyrene nanocomposites prepared from initiator-containing layered double hydroxides of zinc aluminum and magnesium aluminum. Polym Degrad Stab 94:1290–1297 Mayo FR (1978) Long-term properties of polyolefins. Macromolecules 11:492–496 Mc Kellar JF, Allen NS (1979) Photochemistry of Man-Made Polymers, Ltd. Applied Science Published, London 306 S, p 138 Meenakshi P, Noorjahan SE, Rajini R, Venkateswarlu U, Crose S (2002) Mechanical and microstructure studies on the modification of CA film by blending with Polystyrene. Indian Academy of Sciences 25(1):25–29 Mill TR, Richarason H, Mayo FR (1978) J Polym Sci Al 11:2899–2908 Olson DR, Schroeter SH (1978) UV screen progenitors Thermally labile urethane derivatives of hydroxyphenylbenzotriazoles and hydroxybenzophenones. J Appli Poly Sci 22:2165–2176 Osawa Z, Nagashima K, Ohshima H, Cheu E (1979) Study of the degradation of polyurethanes the effect of various additives on the photodegradation of polyurethanes. J Polym Sci 17:409–419 Pantano IAG, Diaz MF, Brandolin A, Sarmoria C (2009) Mathematical modeling of the catalytic degradation of polystyrene in the presence of aluminum chloride. Polym Degrad Stab 94:566–574 Patel P (2007) Additive primer, blown films, cast films and extraction coating, PLACK conference., pp 16–20 Pinto L, Goi B, Schmitt C, Neumann M (2013) Photodegradation of polystyrene films containing UV-visible sensitizers. Journal of Research Updates in Polymer Science 2:39–47 Pospisil J, Nespurek S (2000) Addcon World 2006. Prog Polymer Science 25:1261–1335 Pospisil J, Habicher W, Zweifel H, Pilar J, Nespurek S, Piringer O (2002) Polymer and polymer composites. AAA 10:37–42 Pospisil J, Pilar J, Billingham NC, Marek A, Horak Z, Nespurek S (2006) Factors affecting accelerated testing of polymer photostability. Polymer Degradation Stabilization 91:417–422 Potts JE (1991) Plastic environmentally degradation, The Kirk-Othmer Encyclopedia of Chemical Technology, 3rd edn., Supp. Vol Pushpadass H, Weber R, Dumais J, Hanna M (2010) Biodegradation characteristics of starch- polystyrene loose-fill foams in a composting medium. Bioresour Technol 101(19):7258–7264 Rabek JF (1974) In: Bamford CH, Tipper CF (eds) Comprehensive Chemical Kinetics, vol 14. Elsevier, Amsterdam, p 425 Rabek JF (1987) Mechanism of Photophysical Process and Photochemical Reaction in polymers. John Wiley and Sons, New York

Yousif and Haddad SpringerPlus 2013, 2:398 http://www.springerplus.com/content/2/1/398

Rabek JF (1993) Polymer photodegradation–mechanism and experimental methods. Chapman and Haal, London Rabek JF (1994) Polymer Degradation Mechanisms and experimental methods. Springer, Stocholm Rabek JF (1995) Polymer photodegradation-mechanisms and experimental methods. Chapman Hall, Cambridge Rabek JF (1996) Polymer photodegradation of polymers: physical characteristic and applications. Springer- verlag, Beelin Rabek J, Ranby B (1974a) Studied on the photooxidation mechanism of polymers, photolysis and photooxidation of polystyrene. Journal of polymer science 12:273–291 Rabek JF, Ranby B (1974b) Polymer photophysics and photochemistry: an introduction to the study of Photoprocess of macromolecules. J Polym Sci Al 12:273–281 Rabek JF, Ranby B (1975) Photodegradation, photooxidation and Photostabilization of Polymers. John Wiley, New York Rabie ST, Mahran AM, Kamel EM, Abdel Hamid NH (2008) Photodegradation of polystyrene stabilized with uracil derivative. Journal of applied sciences research 4(12):2015–2026 Ranby BG, Rabek JF (1975a) Photodegradation, Photooxidation and Photostabilization of Polymers. John Wiley & Sons, London, pp 101–102 Ranby B, Rabek JF (1975b) Photodegradation, Photooxidation and Photostabilization of Polymers. Wiley periodicals, Inc, pp 165–184 Ranby B, Rabek JF (1981) In: Garnar DP, Stahl GA (eds) The effects of Hostile Environment on Coatings and Plastics. ACS Symp. Ser, ACS Washington, D.C, pp 291–301 Rnby B, Lucki J (1980) New aspects of photodegradation and photooxidation of PS. Pure & Appl Chem 52:295–303 Ruoko (2012) Uv light induced degradation of polyethylene and polystyrene – spectroscopic and DSC study. Tampere University of Technology, Msc thesis Safy Eldin NM, El-laithy SA (1994) Photooxidative degradation of polystyrene of cover signals lamp of some automobile. Journal of applied polymer science 55:47–54 Saitoh A, Amutharani D, Yamamoto Y, Tsujita Y, Yoshimizu H, Okamoto S (2003) Structure and properties of the mesophase of syndiotactic polystyrene IV. Release of guest molecules from δ form of syndiotactic polystyrene by time resolved FT-IR and WAXD measurement. Polym J 35(11):868–871 Sampers J (2002) Polymer Degradation Stablization 67:455–463 Sastre R, Claramunt RC, Catalina FD, Mateo JL, Santa-Maria MD, Catalan J (1991) Mechanism of photostabilization of polystyrene film by dihydroxyphenylpirazole. J polym Sci A; polymChem 28:3661–3663 Sastre R, Catalina F, Mateo JL, Claremunt R, Santa-Maria MD, Catalan J (2003) Mechanism of photostabilization of polystyrene film by dihydroxypirazoles. J of Polym Sci Part A: Polym Chem 28(13):3661–3668 Schmitt RG, Hirt RC (1963) Handbook of hydroxybenzophenones. J Appl Polym Sci 7:1565–1573 Schnabel W (1981) Polymer Degradation: Principle and Practical Applications. Chapter 14. Hanser Int, München Scott G (2000) Green polymers. Polymer Degradation and Stabilization 68:1–7 Senna M, Hamid H, Hussein M (2002) Nuclear instrument methods. Phys Res Section B 187:48–55 Shao Q, Wang L, Wang X, Yang M, Ge S, Yang X, Wang J (2013) Hydrothermal synthesis and photocatalytic property of porous CuO hollowmicrospheres via PS latex as templates. Solid State Sci 20:29–35 Singh B, Sharma N (2008) Mechanistic implications of plastic degradation. Polym Degrad Stab 93:561–584 Strlic M, Kolar J (2005) Aging and stabilization of papers. Distributed by the National and university Library, Turjaška 1, 1000 Slovenia Sun G, Jang H, Kaang S, Chae K (2002) A new polymeric HALS: preparation of an addition polymer of DGEBA–HALS and its photostabilizing effect. Polymer 43:5855–5863 Szwarc M (1956) The action of carbon black in stabilizing polymeric materials. J Polym Sci 19:462–589 Trozzolo AM, Winslow FH (1968) Macromolecules. American chemical society publishing 98 Uhl FM, Wilkie CA (2002) Polystyrene/graphite nanocomposites: effect on thermal stability. Polym Degrad Stab 76:111–122 Valkoa L, Kleinb E, Kovarikb P, Simonb P (2001) HPLC stanovenie sacharidov v procese modelovaného zrýchleného starnutia papiera. Eur Polym J 37:1123–1133 Vinhas GM, Souto Maiora RM, Lapa CM, Almeida YMB (2003) Degradation studies on plasticized PVC films submitted to gamma radiation. Mat Res 6:497–500

Page 32 of 32

Watson WF (1953) Principles of polymer engineering rheology. Trans IRI 29:29–32 Weidner S, Kuhn G, Freiedrich J, Schroder H (1996) Plasmaoxidative and chemical degradation of poly(ethylene terepthalate) studied by matrix-assisted laser desorption/ionisation mass spectrometry. Rapid Communications in Mass Spectrometry 10(1):40–46 Weir NA (1978) New aspect of photodegradation and photooxidation of polystyrene. Europ Polym J l4:9–14 Wiles DM (1979) Photostabilisation mechanisms in polymers: A review. Pure Appli Chem 50:291 Wiles DM, Carlsson DJ (1980) Photostabilisation mechanisms in polymers: A review. Polym Deg Stabil 3:61–72 Williams FR, Jordan MW, Dannerberg EM (1969) Reinforcement of elastomers by fillers: Review. J Appl Polym Sci 9:861–871 Willis PB (1984) Investigation of test method material properties and processes for solar cell in capsulation, eighth annual report Winslow FH, Matreyek W, Trozzolo AM (1969) Particle size distribution and morphology of in situ suspension polymerized toner. Amer Chem Soc Polymer Prepr 10:1271 Wypych G (2008) Handbook of material weathering, 4th edn. Chemtec Publishing, Toronto Yousif E (2010) Photostabilization of PVC by inorganic complexes. LAP LAMBERT academic publishing Yousif E (2012) Photostabilization of thermoplastic polymers. Lambert Academic Publishing, Germany Yousif E, Salimon J, Salih N (2011a) New stabilizer for polystyrene based on 2-N-Salicylidene-5-(substituted)-1,3,4-thiadiazole compoundes. Journal of Saudia Chemical Society 16(3):299–306, A Yousif E, Salimon J, Salih N (2011b) Photostability of poly (vinyl chloride). Dr. Muller publisher, VDM Verlag, B Yousif E, Salimon J, Salih N (2012) New stabilizer for polystyrene based on 2-Thioacetic Acid Benzothiazol complexes. Journal of applied polymer Science 125:1922–1927 Yousif E, Hameed A, Salih N, Salimon J, Abdullah BM (2013) New photostabilizers for polystyrene based on 2,3-dihydro-(5-mercapto-1,3,4-oxadiazol-2-yl)phenyl-2-(substituted)-1,3,4-oxazepine- 4,7-dione compounds. SpringerPlus Journal 1–8 Zweifel H (1998) Stabilization of polymeric materials. Berlin Heidelberg, Springer-Verslag doi:10.1186/2193-1801-2-398 Cite this article as: Yousif and Haddad: Photodegradation and photostabilization of polymers, especially polystyrene: review. SpringerPlus 2013 2:398.

Submit your manuscript to a journal and beneﬁt from: 7 Convenient online submission 7 Rigorous peer review 7 Immediate publication on acceptance 7 Open access: articles freely available online 7 High visibility within the ﬁeld 7 Retaining the copyright to your article

Submit your next manuscript at 7 springeropen.com

Photodegradation and photostabilization of polymers, especially polystyrene: review. - PDF Download Free (2024)

FAQs

What is photo degradation of polystyrene? ›

Photodegradation of polystyrene in air causes discoloration (yellowing), cross-linking, and chain scission due to oxidation. A photodegradation process was also proposed on the basis of the IR spectrum of the photoirradiated film, which indicated the formation of peroxy radical and hydroperoxide intermediates.

View Details ›

What is the photooxidation of polystyrene? ›

Polystyrene is observed to yellow during photo-oxidation, which is attributed to the formation of polyenes from these terminal alkenes.

Read The Full Story ›

What is photodegradation of polymers in photochemistry? ›

Photodegradation of a polymer is in most cases initiated by chromophores which are extraneous groups on the chains, e.g. formed by oxidation, or impurities which can be metal ions, organometallic compounds, light-absorbing organic compounds or solid particles which absorb light.

Discover More ›

Is photodegradation good? ›

Light degradation is often deliberately avoided because it can damage paintings and other items [23]. However, this process is partly responsible for biomass remineralization and is specifically used in certain disinfection techniques [24].

Learn More Now ›

How long does photodegradation take? ›

On the whole, this is an incredibly lengthy process, often taking as much as 50 years or more for the sun to completely break down the plastic and for the microbes to assimilate the polymer molecules. This process becomes even more arduous and protracted when it takes place underwater.

Get More Info Here ›

How many years does it take for polystyrene to decompose? ›

Once in the landfill, it does not decompose quickly. Some estimates put the lifespan of styrofoam in a landfill around 500 years, and some put it way beyond that.

What are the advantages of photodegradation? ›

The advantages of photodegradation methods include simplicity, efficiency, cost-effectiveness, safety, and environmental friendliness. Photodegradation techniques utilize light sources such as LED blue visible light ¹, natural sunlight ⁵, and visible light illumination ⁴ to degrade pollutants in wastewater.

View Details ›

How does photodegradation affect plastics? ›

The most common is the effect of UV radiation (photodegradation) that makes the plastics brittle and as a result the plastics fragment. In the end, if there's complete breakdown, plastics is degraded in CO2, water, methane, hydrogen, etc.

See Details ›

What is the main drawback of photodegradable plastic? ›

Photodegradable plastics tend to break down into small particles of plastic rather than decomposing completely. The idea is that these small pieces will then biodegrade. Unfortunately, they are often not biodegradable and so remain in the environment.

Get More Info ›

What are the cons of photocatalysis? ›

One major drawback is the fast recombination of photogenerated charge carriers, which leads to poor photocatalytic efficiency . Another limitation is the low utilization of solar energy and high recombination rate of photogenerated charges, which limits its large-scale application .

Learn More Now ›

What is the difference between photocatalysis and photodegradation? ›

Photocatalysis: is the science that involves use of both catalysts and light. Photo-catalytic degradation: Is a specific application of photocatalysis. Specifically in the case of degradation of contaminants or pollutants (generally in the liquid phase).

Photodegradation and photostabilization of polymers, especially polystyrene: review. - PDF Download Free (2024)

FAQs

What is photo degradation of polystyrene? ›

What are the advantages of photodegradation? ›

References